Flexiclad ER – Elastomeric polymer composite repairs, resurface & protects flexible components.
- Country Origin: USA
- Working Life: 12′ – 50′ depend on the environment temperature
- Shelf life: Indefinite
-
Use for...
-
Conveyor Belts
-
Hoses
-
Damaged Sidewalls On Off Road Tires
-
Resilient Bonding of Metals, Woods, etc.
-
Creating / Repairing Flexible Seals, Gaskets & Seats
-
Expansion Bellows
REVOLUTIONARY ELASTOMERIC POLYMER COMPOSITE REPAIRS, RESURFACES & PROTECTS FLEXIBLE COMPONENTS.
FLEXICLAD ER is a two component, 100% solids, trowelable polymer composite that has been specifically formulated to repair damaged flexible components such as conveyor belts, hoses, off-road tire sidewalls, etc.
FLEXICLAD ER is a very unique material that requires no primer, bonds to most rubber / flexible materials and cures at ambient temperatures – no heat is required. It is safe and simple to use and no special tools are needed. It can be used to create irregular flexible gaskets on distorted flange faces or to create a resilient bond for metal, wood, etc. It can also be used to seal / caulk heat exchanger water boxes to tube sheet faces or to seal joints in condensate pans, cooling tower pans, etc. FLEXICLAD ER is an indispensable addition to any maintenance engineer’s tool box.
FLEXICLAD ER is ideal for sealing joints and seams on machinery and equipment that are prone to vibration or movement – and wherever flexible repairs are required
| Volume capacity / 250g unit: 14.1 in3 / 233 cm3 |
|---|
| Mixed density : 0.039 lbs per in3 / 1.07 gm per cc |
| Coverage rate / 250 g unit: 730 cm2, @ 3mm |
| Shelf life : Indefinite |
| Volume Solids : 100% |
| Mixing ratio Base / Activator / Aggregate (volume) 2 / 1 |
| Mixing ratio Base / Activator (weight) : 1.8 / 1 |
| Working Life 25ºC : 16 min |
| Return to Service 25ºC : 3 h |
| Full Cure : 72 h |
| Hardness – Shore D |
|---|
| (ASTM D-1002) : 500 psi (35 kg/cm2) |
| (ASTM D-1002) : 500 psi (35 kg/cm2) |
| (ASTM D-2240) : 15 |
| (ASTM D-2370) : 150% |
| (ASTM D-4541) : 300 psi (21 kg/cm2) – concrete failed |
| Elongation |
| Note: Adhesion to most rubber substrates when properly prepared is greater than the cohesive strength of the rubber substrate. |
| Pull-Off Strength on Concrete |
| Tensile Shear Adhesion aluminum |
| Tensile Shear Adhesion steel |
| Acetic acid 0-10% —– G |
|---|
| Aviation fuel (nhiên liệu máy bay) —– G |
| Butyl alcohol (N-butanal) —– G |
| Canxi clorua —– EX |
| Clohydric acid (0-10%) —– G |
| Clohydric acid (10-20%) —– G |
| Crude Oil / Dầu mỏ —– EX |
| Diesel fuel / Dầu diezel —– EX |
| Ethanol (Ethyl alcohol) —– G |
| Gasoline / Xăng —– G |
| Phosphoric acid (0-10%) —– EX |
Technical data
| Volume capacity / 250g unit: 14.1 in3 / 233 cm3 |
|---|
| Mixed density : 0.039 lbs per in3 / 1.07 gm per cc |
| Coverage rate / 250 g unit: 730 cm2, @ 3mm |
| Shelf life : Indefinite |
| Volume Solids : 100% |
| Mixing ratio Base / Activator / Aggregate (volume) 2 / 1 |
| Mixing ratio Base / Activator (weight) : 1.8 / 1 |
| Working Life 25ºC : 16 min |
| Return to Service 25ºC : 3 h |
| Full Cure : 72 h |
Physical properties
| Hardness – Shore D |
|---|
| (ASTM D-2240) : 15 |
| Elongation |
| (ASTM D-2370) : 150% |
| Tensile Shear Adhesion steel |
| (ASTM D-1002) : 500 psi (35 kg/cm2) |
| Tensile Shear Adhesion aluminum |
| (ASTM D-1002) : 500 psi (35 kg/cm2) |
| Pull-Off Strength on Concrete |
| (ASTM D-4541) : 300 psi (21 kg/cm2) – concrete failed |
| Note: Adhesion to most rubber substrates when properly prepared is greater than the cohesive strength of the rubber substrate. |
Chemical resistance
| Acetic acid 0-10% ----- G |
|---|
| Aviation fuel (nhiên liệu máy bay) ----- G |
| Butyl alcohol (N-butanal) ----- G |
| Canxi clorua ----- EX |
| Crude Oil / Dầu mỏ ----- EX |
| Diesel fuel / Dầu diezel ----- EX |
| Ethanol (Ethyl alcohol) ----- G |
| Gasoline / Xăng ----- G |
| Clohydric acid (0-10%) ----- G |
| Clohydric acid (10-20%) ----- G |
| Phosphoric acid (0-10%) ----- EX |
| Potassium Chloride (Kali Clorua) ----- G |
| Sodium chloride (Natri Clorua) ----- EX |
| Sulfuric acid (0-10%) ----- EX |
| Sulfuric acid (10-20%) ----- G |