Flexiclad LC – Elastomeric Expansion Joint Compound for Horizontal Surfaces
- Country Origin: USA
- Working Life: 45′ – 60′ depend on the environment temperature
- Shelf life: Indefinite
| Volume capacity / 0.5 kg: 28 in3 / 460 cm3 |
|---|
| Mixed density : 0.036 lbs per in3 / 1.08 gm / cc |
| Shelf life : Indefinite |
| Volume Solids : 100% |
| Mixing ratio Base / Activator / Aggregate (volume) 3 / 2 |
| Mixing ratio Base / Activator (weight) : 5 / 3 |
| Working Life 25ºC : 60 min |
| Return to Service 25ºC : 4 h |
| Full Cure : 72 h |
| Hardness – Shore D |
|---|
| (ASTM D-1002) : 1200psi (84 kg/cm2) |
| (ASTM D-1002) : 1300 psi (91 kg/cm2) |
| (ASTM D-2240) : 60 |
| (ASTM D-2370) : 700% |
| (ASTM D-4541) : 300 psi (21 kg/cm2) – concrete failed |
| Elongation |
| Pull-Off Strength on Concrete |
| Tensile Shear Adhesion aluminum |
| Tensile Shear Adhesion steel |
| Gasoline / Xăng —– EX |
|---|
| Clohydric acid (0-10%) —– G |
| Phosphoric acid (0-10%) —– EX |
| Sodium chloride (Natri Clorua) —– EX |
| Sodium hydroxide (Natri Hidroxit) —– EX |
| Axit Sulfuric (0-10%) —– EX |
| Bleach / Chất tẩy trắng —– EX |
| Dung môi Ethylene Glycol (0-50%) —– EX |
| EX – Suitable for most applications including immersion |
| G – Suitable for intermittent contact splashes etc |
| NR – Not Recommended |
Technical data
| Volume capacity / 0.5 kg: 28 in3 / 460 cm3 |
|---|
| Mixed density : 0.036 lbs per in3 / 1.08 gm / cc |
| Shelf life : Indefinite |
| Volume Solids : 100% |
| Mixing ratio Base / Activator / Aggregate (volume) 3 / 2 |
| Mixing ratio Base / Activator (weight) : 5 / 3 |
| Working Life 25ºC : 60 min |
| Return to Service 25ºC : 4 h |
| Full Cure : 72 h |
Physical properties
| Hardness – Shore D |
|---|
| (ASTM D-2240) : 60 |
| Elongation |
| (ASTM D-2370) : 700% |
| Tensile Shear Adhesion steel |
| (ASTM D-1002) : 1300 psi (91 kg/cm2) |
| Tensile Shear Adhesion aluminum |
| (ASTM D-1002) : 1200psi (84 kg/cm2) |
| Pull-Off Strength on Concrete |
| (ASTM D-4541) : 300 psi (21 kg/cm2) – concrete failed |
Chemical resistance
| Gasoline / Xăng ----- EX |
|---|
| Clohydric acid (0-10%) ----- G |
| Phosphoric acid (0-10%) ----- EX |
| Sodium chloride (Natri Clorua) ----- EX |
| Sodium hydroxide (Natri Hidroxit) ----- EX |
| Axit Sulfuric (0-10%) ----- EX |
| Bleach / Chất tẩy trắng ----- EX |
| Dung môi Ethylene Glycol (0-50%) ----- EX |
| EX – Suitable for most applications including immersion |
| G – Suitable for intermittent contact splashes etc |
| NR – Not Recommended"""" |
ELASTOMERIC EXPANSION JOINT COMPOUND FOR HORIZONTAL SURFACES
FLEXICLAD LC® is a two component, 100% solids, pourable elastomeric polymer composite that has been specifically formulated to seal expansion joints in concrete as well as other cementitious / mineral substrates including tiles, brick, slate, stone, etc. It also bonds very well to metal and wood surfaces.
FLEXICLAD LC requires no primer, bonds to most rigid substrates and cures at ambient temperatures. It has been specifically designed to resist countless freeze / thaw cycles – stretching to well over 600%. It is excellent for sealing between dissimilar materials which may expand and contract at different rates. It also has very good chemical resistance making it the ideal choice for use in secondary containment areas as well as production floors, loading docks, etc.
FLEXICLAD LC incorporates revolutionary polyaspartic technology for sealing expansion joints where durability and flexibility are uniquely important: