CeramAlloy HTL – outstanding erosion/corrosion resistance at elevated temperatures

  • Country Origin: USA
  • Working Life: 25′ – 90′ depend on the environment temperature
  • Shelf life: Unlimited
Require quote
  • Z

    Apply by Brush, Roller or Flexible Applicator
  • Z

    Requires No Heat
  • Z

    Unlimited Shelf Life
  • Z

    100% Solids
  • Z

    Safe & Simple To Use

  • Repairs and Protects...
  • Z

    Heat Exchanger Tube Sheets & Water Boxes
  • Z

    Drum Dryers
  • Z

    Pumps,
  • Z

    Valves & Pipework Housings & Tanks

The advantage of high performance polymer composites technologies used for repairing, resurfacing, industrial maintenance and fluid flow problems are saving you time, money cause quickly cures, easy to check the surface & temperature monitoring in plate instead waiting for full cure as the traditional.

 

 

A RECOGNIZED WORLD LEADER IN ADVANCED POLYMER TECHNOLOGIES.

OUTSTANDING EROSION/CORROSION RESISTANCE – EVEN AT ELEVATED TEMPERATURES!

METALCLAD® CeramAlloy® HTL is a two component, 100% solids, liquid polymer composite used for repairing, resurfacing and coating both damaged and new components to provide outstanding erosion and corrosion resistance at elevated temperatures.

When mixed, CeramAlloy® HTL is a viscous liquid. CeramAlloy® HTL cures to a hard, ceramic-like material with an extremely smooth surface finish. It has been specifically developed for elevated temperature applications.

METALCLAD® CeramAlloy® HTL is a High Performance Polymer Composite for resurfacing and protecting all types of fluid flow equipment from aggressive erosion and corrosion damage especially at elevated temperatures.

Technical data
Physical properties
Chemical resistance

Technical data

Volume capacity per kg / Thể tích / kg : 38 in3 / 629 cc
Mixed density / Khối lượng riêng (tỉ trọng) sau khi trộn : 0.057 lbs per in3 / 1.59 gm per cc
Coverage rate per kg. @ 12 - 15 mils / Diện tích phủ 1kg :  1.4 m2  @0.3 - 0.35 mm
Shelf life / Thời gian lưu kho : Indefinite / vô thời hạn
Volume Solids / Thể tích đóng rắn : 100% 
Mixing ratio / Tỷ lệ trộn Base / Activator (volume / theo thể tích) 3 / 1
Mixing ratio / Tỷ lệ trộn Base / Activator (weight / theo trọng lượng) : 4.6 /1
Working Life / Thời gian thi công ở 25ºC : 40 phút
Cure Times / Thời gian đóng rắn ở 25ºC : 10 giờ
Full cure / Thời gian đóng rắn hoàn toàn ở 25ºC : 18 giờ
Chemical Immersion / Ngâm trong hóa chất : 72 giờ

Physical properties

Compressive strength / Chịu lực (độ bền) nén
ASTM D-695 :  12,000 psi (840 kg/cm2)
Flexural strength / Chịu lực (độ bền) uốn
ASTM D-790 : 8,500 psi (595 kg/cm2)
ĐộHardness - Shore D / Độ cứng shore D cứng shore D 
ASTM D-2240: 87
Tensile Shear Adhesion steel / Độ bền cắt bám dính trên thép
ASTM D-1002 : 4,000 psi (280 kg/cm2)
Tensile Shear Adhesion aluminum / Độ bền cắt bám dính trên nhôm
ASTM D-1002 : 2,500 psi (175 kg/cm2)
Tensile Shear Adhesion copper / Độ bền cắt bám dính trên đồng
ASTM D-1002 : 3,000 psi (210 kg/cm2)
Tensile Shear Adhesion copper / Độ bền cắt bám dính trên đồng
ASTM D-1002 : 4,100 psi (287 kg/cm2)
Temperature Guidelines / Chịu nhiệt độ:
Dry / Khô - 520ºF / 270ºC
Wet / Ướt - 330ºF / 165ºC

Chemical resistance

Ammonium hydroxide (amoniac) (0-5%) ----- EX
Sulfuric acid / Axit Sulfuric (50%) ----- EX
Sulfuric acid / Axit Sulfuric (98%) ----- G
Hydrochloric acid / HCL (20%) ----- G
Crude oil / Dầu động cơ ----- EX
Sodium chloride / NACL (5%) ----- EX
EX – Suitable for most applications including immersion
G – Suitable for intermittent contact splashes etc
NR – Not Recommended""""