CeramAlloy CP+ outstanding erosion/corrosion resistance nuclear environment

  • Country Origin: USA
  • Working Life: 40′ – 240′ depend on the environment temperature
  • Shelf life: Unlimited
Require quotation
  • Z

    Trowelable
  • Z

    Requires No Heat
  • Z

    Extremely Adhesion
  • Z

    100% solids
  • Z

    Unlimited Shelf Life
  • Z

    resurfacing, protecting components from aggressive erosion, corrosion damage.

REPAIRS DEEP EROSION/CORROSION DAMAGE. COLD CURING, SAFE TO USE AND EASILY APPLIED.

Cures to a Metal Hard, Ceramic-Like Finish.

NUCLEAR D.B.A. Tested ASTM 3911-89

METALCLAD CeramAlloy CP+ is a two component, 100% solids, high-performance polymer composite specifically formulated to provide effective repair and rebuilding characteristics on all types of fluid flow equipment.

METALCLAD CeramAlloy CP+ is a paste when mixed, so it is easily applied. When cured, however, CP+ becomes a metal-hard, ceramic-like compound.

METALCLAD CeramAlloy CP+ is the best material to use when making repairs to areas deeply damaged by erosion/corrosion environments on all types of fluid flow components.

Technical data
Physical properties
Chemical resistance
Technical data
Volume capacity per kg / Thể tích / kg : 30 in3 / 492 cc
Mixed density / Khối lượng riêng (tỉ trọng) sau khi trộn : 0.073 lbs per in3 / 2.03 gm per cc
Coverage rate per kg. @6mm / Diện tích phủ / kg: 120 in2 / 0.077 m2 @6mm
Shelf life / Thời gian lưu kho :  Indefinite / vô thời hạn
Volume Solids / Thể tích đóng rắn : 100%
Mixing ratio / Tỷ lệ trộn Base / Activator / Aggregate (theo thể tích) : 2 / 1
Mixing ratio / Tỷ lệ trộn Base / Activator (theo trọng lượng) : 3.5 / 1
Working Life / Thời gian thi công ở 25ºC : 60 phút
Cure Times / Thời gian đóng rắn ở 25ºC : 6 giờ
Full Cure / Thời gian đóng rắn hoàn toàn ở 25ºC : 24 giờ
Chemical Immersion / Ngâm trong hóa chất : 72 giờ
Physical properties
Compressive strength / Chịu lực (độ bền) nén
(ASTM D-695) : 14,000 psi (980 kg/cm2)
Flexural strength / Chịu lực (độ bền) uốn
(ASTM D-790) : 15,500 psi (1085 kg/cm2)
Hardness - Shore D / Độ cứng shore D
(ASTM D-2240) : 82
Tensile Shear Adhesion steel / Độ bền cắt bám dính trên thép
ASTM D-1002 : 2,900 psi (203 kg/cm2)
Tensile Shear Adhesion aluminum / Độ bền cắt bám dính trên nhôm
ASTM D-1002 : 2,750 psi (193 kg/cm2)
Tensile Shear Adhesion copper / Độ bền cắt bám dính trên đồng
ASTM D-1002 : 2,400 psi ( 168 kg/cm2 )
Tensile Shear Adhesion stainless steel / Độ bền cắt bám dính trên thép không rỉ
ASTM D-1002 : 3,300 psi (231 kg/cm2)
Surface resistivity / Suất điện trở mặt
ASTM D-257 : 1 x 1015 ohms
Volume resistivity / Suất điện trở khối
ASTM D-257 : 1 x 1015 ohm/cm
Dielectric constant / Hằng số điện môi : 7.5
(ASTM D-150) Dielectric Constant
Dielectric strength / Độ bền điện môi
ASTM D-115 Dielectric Strength : 500 V / Mil
Breakdown Voltage / Điện áp đánh thủng
ASTM D-149 method A / phương pháp A : 18.6 Kv
Chemical resistance
Acetic acid0-10%: ----- EX Methanol ----- G
Aceton ----- GMineral Oil / Dầu khoáng ----- EX
Aviation fuel (nhiên liệu máy bay)  ----- EXNitric acid / Axit Nitric (0-10%) ----- EX
Butyl alcohol (N-butanal) ----- EXNitric acid / Axit Nitric (10-20%) ----- G
Calcium chloride / Canxi clorua ----- EXPhosphoric acid / Axit Phosphoric (0-10%) ----- G
Crude oil / Dầu mỏ. ----- EXPotassium chloride / Potassium Chloride (Kali Clorua) ----- EX
Diesel fuel / Dầu diezel ----- EXPropyl alcohol / Dung môi IPA (Rượu isopropanol) ----- EX
Ethyl alcohol / Ethanol ----- GSodium chloride / Natri Clorua ----- EX
Gasoline / Xăng ----- EXSodium hydroxide / Natri Hidroxit ----- EX
Heptan (Heptane, Dipropyl Methan) ----- EXSulfuric acid / Axit Sulfuric (0-10%) ----- EX
Hydrochloric acid / Axit Clohydric (0-10%) ----- EXSulfuric acid / Axit Sulfuric (10-20%) ----- G
Hydrochloric acid / Axit Clohydric (10-20%) ----- GToluen (Metylbenzen) ----- EX
Kerosene / Dầu hỏa ----- EXXylene ----- EX
EX – Suitable for most applications including immersion
G – Suitable for intermittent contact splashes etc
NR – Not Recommended""""