CeramAlloy CBX – abrasion resistance & extend the service life

  • Country Origin: USA
  • Working Life: 15′ – 30′ depend on the environment temperature
  • Shelf life: unlimited
Require quotation
  • Z

    Extraordinary Abrasion Resistance
  • Z

    Trowelable
  • Z

    Unlimited Shelf Life
  • Z

    100% Solids
  • Z

    Safe & Simple To Use

  • Use for...

  • Z

    Elbows, Pumps,
  • Z

    Chutes, Vibratory Feeders
  • Z

    Cyclones, Separators
  • Z

    Pipe, Water Boxes, Housings & Tanks,...

REPAIR AND PROTECT ALL TYPES OF EQUIPMENT SUBJECT TO VERY AGGRESSIVE ABRASION.

Engineered to repair deeply damaged components.

METALCLAD CeramAlloy CBX is a three component, 100% solids, polymer composite specifically formulated to provide effective repair and rebuilding characteristics on all types of equipment subject to severe abrasion.

METALCLAD CeramAlloy CBX is a paste when mixed, so it is easily applied. When cured, however, CBX becomes a metal-hard, highly abrasion resistant compound engineered to repair deeply damaged components in the most aggressive abrasive environments.

METALCLAD CeramAlloy CBX is the best material to use to protect equipment subject to very aggressive abrasive environments.

Elbows, Pipes, Pumps, Chutes, Deflector Plates, Cyclones, Separators, Vibratory Feeders, Transfer Augers, etc.

Technical data
Physical properties
Chemical resistance

Technical data

Volume capacity per 5 kg / Thể tích / 5 kg : 110 in3 / 1790 cc
Mixed density / Khối lượng riêng (tỉ trọng) sau khi trộn : 0.100 lbs / in3 (2.76 gm / cc)
Coverage rate per 5 kg. @ 200 mils / Diện tích phủ / 5kg: 3.78 ft2 / 0.35 m2 (độ dày 5 mm)
Shelf life / Thời gian lưu kho : Indefinite / vô thời hạn
Volume Solids / Thể tích đóng rắn: 100%
Mixing ratio / Tỷ lệ trộn Base / Activator / Aggregate (by volume / theo thể tích) : 5 / 2 / 14
Tỷ lệ trộn Base / Activator (by weight / theo trọng lượng) : 7 / 2 / 20
Working Life / Thời gian thi công ở 25ºC : 20 phút
Cure Times / Thời gian đóng rắn ở 25ºC : sau 24 giờ
Full Cure/ Thời gian đóng rắn hoàn toàn ở 25ºC : sau 48 giờ

Physical properties

Compressive strength / Chịu lực (độ bền) nén
(ASTM D-695) : 16,000 psi (1125 kg/m2)
Flexural strength / Chịu lực (độ bền) uốn
(ASTM D-790) : 6,000 psi (422 kg/cm2)
Hardness - Shore D / Độ cứng shore D
(ASTM D-2240) : 86
Tensile Strength / Độ bền kéo
(ASTM D-2370) : 2,500 psi (176 kg/cm2)
Tensile Shear Adhesion steel / Độ bền cắt bám dính trên thép
(ASTM D-1002) : 4,000 psi (280 kg/cm2)
Tensile Shear Adhesion aluminum / Độ bền cắt bám dính trên nhôm
(ASTM D-1002) : 2,500 psi (175 kg/cm2)
Tensile Shear Adhesion copper / Độ bền cắt bám dính trên đồng
(ASTM D-1002) : 3,000 psi (210 kg/cm2)
Tensile Shear Adhesion stainless steel / Độ bền cắt bám dính trên thép không rỉ
(ASTM D-1002) : 4,100 psi (287 kg/cm2)

Chemical resistance

Acetic acid0-10%: ----- G Methanol ----- G
Ammonium hydroxide (amoniac) (0-10%) ----- EXMineral Oil / Dầu khoáng ----- EX
Aviation fuel (nhiên liệu máy bay)  ----- EXNitric acid / Axit Nitric (0-10%) ----- EX
Butyl alcohol (N-butanal) ----- EXNitric acid / Axit Nitric (10-20%) ----- G
Calcium chloride / Canxi clorua ----- EXPhosphoric acid / Axit Phosphoric (0-10%) ----- G
Crude oil / Dầu mỏ. ----- EXPotassium chloride / Potassium Chloride (Kali Clorua) ----- EX
Diesel fuel / Dầu diezel ----- EXPropyl alcohol / Dung môi IPA (Rượu isopropanol) ----- EX
Ethyl alcohol / Ethanol ----- GSodium chloride / Natri Clorua ----- EX
Gasoline / Xăng ----- EXSodium hydroxide / Natri Hidroxit ----- EX
Heptan (Heptane, Dipropyl Methan) ----- EXSulfuric acid / Axit Sulfuric (0-10%) ----- EX
Hydrochloric acid / Axit Clohydric (0-10%) ----- EXSulfuric acid / Axit Sulfuric (10-20%) ----- G
Hydrochloric acid / Axit Clohydric (10-20%) ----- GToluen (Metylbenzen) ----- EX
Kerosene / Dầu hỏa ----- EXXylene ----- EX
EX – Suitable for most applications including immersion
G – Suitable for intermittent contact splashes etc
NR – Not Recommended""""